Product Details:
|
| K-Value: | 74 | Brookfield Viscosity: | ≦8000 Cps |
|---|---|---|---|
| Polymerization Degree: | 1,450±100 | Apparent Density: | 0.20~0.30g/cm3 |
Zhongtai P440 PVC Paste Resin Emulsion Grade K-Value 74
Product Specifications
| Attribute | Value |
| Package | 20kg bag |
| Type | Emulsion |
| K-Value | 74 |
| Product name | PVC paste resin |
| Appearance | white powder |
| Brand | Zhongtai |
| Polymerization degree | 1,450±100 |
| Brookfield viscosity | ≦8000 cps |
| Delivery | 15-20 days |
| Payment | LC or TT |
Technical Parameters
| Parameter | Value | Test Method |
| K-Value | 74 | DIN 53726 |
| Polymerization degree | 1,450±100 | JIS K6721 |
| Volatiles | ≦0.50 % | ASTM D3030 |
| Apparent density | 0.20~0.30g/cm3 | ASTM D1895 |
| Brookfield viscosity | ≦8000 cps | ASTM D1824 |
| Severs | ≧200 g/100sec | ASTM D1823 |
Key Features
• Low to medium Brookfield viscosity
• Excellent air release of plastisol
• Excellent weather resistance of color paint
• High thermostability and initial color of products
Product Description
P-440 is a low to medium viscosity of medium molecular weight PVC homopolymer paste resin. It features excellent transparency, thermal stability, water resistance and weather resistance. With high compatibility with plasticizers, organic solvents and fillers, plastisols made with P-440 are ideal for:
• Non-foaming and micro-foam leather
• Glass applications
• Dipping processes
• Metal coating
• Color paint applications
Application Notes
1. Resin 100phr DINP 60phr, hobart N-50 mixed 5min at No1 speed and 15min at No2 speed.
2. Plastisol aged 2hrs at 25℃, measured No.6 spin 50rpm.
3. 2hr plastisol detected on 90psi.