Product Details:
|
| Average Polymerization Degree: | 1335 | B-type Viscosity (30℃, 100PVC:65DOP): | 2410 MPa.s |
|---|---|---|---|
| Impurity Particle Number: | 7 PCS | Mass Fraction Of Volatile Matter: | 0.28 % |
| Highlight: | PVC paste resin K-Value 72,ultra-low volatile PVC resin,stable low plastisol viscosity resin |
||
| Item | Premium Grade Standard | First Grade Standard | Qualified Grade Standard | Test Result |
|---|---|---|---|---|
| Average Polymerization Degree | 1300±100 | 1300±100 | 1300±100 | 1335 |
| B-type Viscosity (30℃, 100PVC:65DOP) | 4000±2500 mPa.s | 4000±2500 mPa.s | 4000±2500 mPa.s | 2410 mPa.s |
| Impurity Particle Number | ≤ 12 pcs | ≤ 20 pcs | ≤ 40 pcs | 7 pcs |
| Mass Fraction of Volatile Matter | ≤ 0.40 % | ≤ 0.50 % | ≤ 0.50 % | 0.28 % |
| Residue on 63 μm Sieve | ≤ 0.1 % | ≤ 0.1 % | ≤ 0.3% | 0.01 % |
| Residual Vinyl Chloride Monomer Content | ≤ 5 μg/g | ≤ 10 μg/g | ≤ 10 μg/g | 4.95 μg/g |
| Scraper Fineness | ≤ 100 μm | -- | -- | 25 μm |
Test Conditions: Paste viscosity test condition: 100 parts PVC : 65 parts DOP
Safety Compliance: Residual vinyl chloride monomer content is mandatory national safety control index
All data in this sheet are official factory inspection certified results, only for technical reference. Actual product performance may vary according to different formulation designs, processing equipment and production operating parameters. Users shall conduct pre-production verification tests before large-scale mass production.