SG-3 Suspension PVC Resin K-Value 58-60
1. Product Introduction
SG-3 is a low-viscosity general-purpose suspension PVC resin. It features low polymerization degree, excellent fluidity, outstanding plasticizer absorption performance and stable thermal processing properties. With low volatile matter, low impurity content and high whiteness, this grade ensures stable high-speed extrusion, injection molding processing, and excellent dimensional stability of finished products. It is widely used in soft and rigid PVC profiles, pipes, cable materials, plastic products and other mass-production scenarios, with reliable batch consistency and superior comprehensive processing performance.
2. Technical Specification & Actual Test Result Table
| Item | Premium Grade Standard | First Grade Standard | Qualified Grade Standard | Test Result |
| Viscosity Number | 127-135 mL/g | ------------------- | ------------------------- | 130 mL/g |
| Impurity Particle Count | ≤ 16 pcs | ≤ 30 pcs | ≤ 60 pcs | 16 pcs |
| Volatile Matter (Including Moisture) | ≤ 0.30 % | ≤ 0.40 % | ≤ 0.50 % | ≤ 0.18 % |
| Apparent Density | ≥ 0.45 g/ml | ≥ 0.42 g/ml | ≥ 0.40 g/ml | 0.50 g/ml |
| Sieve Residue (250μm) | ≤ 1.6 % | ≤ 2.0 % | ≤ 8.0 % | 1.4 % |
| Sieve Pass Rate (63μm) | ≥ 97 % | ≥ 90 % | ≥ 85 % | 99 % |
| Fish Eye Count | ≤ 20 pcs/400cm² | ≤ 30 pcs/400cm² | ≤ 60 pcs/400cm² | ---------- |
| Plasticizer Absorption (Per 100g Resin) | ≥ 26 g | ≥ 25 g | ≥ 23 g | 82 g |
| Whiteness (160℃, 10min) | ≥ 78 % | ≥ 75 % | ≥ 70 % | ≥82 % |
| Water Extract Conductivity | ≤ 5 us·cm/g | ≤ 5 us·cm/g | ----------------- | 2 us·cm/g |
| Residual Vinyl Chloride Content | ≤ 5 μg/g | ≤ 5 μg/g | ≤ 10μg/g | 5 μg/g |
| Appearance | White powder | White powder | White powder | White powder |
3. Product Features & Advantages
• Low viscosity number, excellent melt fluidity, suitable for high-efficiency injection & extrusion molding
• Ultra-low volatile matter and impurity particles, effectively reduce product surface defects
• High plasticizer absorption rate, fast plasticizing speed and stable mixing performance
• High whiteness and low conductivity, good thermal stability and long service life
• Low residual VCM content, meeting national environmental protection and safety standards
• Uniform particle distribution, stable batch quality, adaptable to various PVC formula systems
4. Typical Application Fields
PVC wire & cable materials, soft and rigid pipe fittings, plastic steel profiles, injection molded parts, color masterbatch carriers, various general soft & hard PVC finished products.
5. Technical Statement
All data in this sheet are official factory inspection results for reference only. Actual performance may vary due to different formula designs, processing equipment and production operating conditions. Users are recommended to conduct pre-production tests to verify product suitability before mass bulk production.