K-value:65-68
Volatile matter (including water):≤ 0.5 %
Number of impurities and foreign particles:≤ 30 pcs
Residual Vinyl Chloride Monomer Content:2.63 μg/g
Scraper Fineness:21 μm
B-type Viscosity (30℃, 100PVC:65DOP):2840 mPa.s
Average Polymerization Degree:1335
B-type Viscosity (30℃, 100PVC:65DOP):2410 mPa.s
Impurity Particle Number:7 PCS
Average Polymerization Degree:1676
Impurity Particle Number:8PCS
Mass Fraction of Volatile Matter:0.29%
Apparent Density:0.50 g/ml
Sieve Pass Rate (63μm):99%
Plasticizer Absorption (Per 100g Resin):82g
Standard Paste Viscosity (B-type, 50r/min):2660 mpa.s
Volatile Matter (including moisture):0.16 %
Impurity Particle Number:4pcs
Polymerization degree:1270
Number of impurity particles:7PCS
Moisture & volatile matter content:0.33 %
Residual vinyl chloride monomer:4 μg/g
Impurity particle number:4pcs
Volatile matter (including water):0.31 %
Polymerization degree:1270
Number of impurity particles:7PCS
Moisture & volatile matter content:0.33 %
Degree of Polymerization:980 – 1040
K-Value:66 – 68
Impurity Particles:≤ 16 pcs
Polymerization degree:1300±100
Brookfield viscosity (PVC:DOP=100:65, 30℃, 1h):1500 ~ 6500 mPa·S
Number of impurity particles:≤ 20pcs
Sieving rate (49 μm sieve pore):≥ 99%
Whiteness (160°C, 10min):≥ 76%
Foreign particle number:≤ 20 pcs