TiO₂ content:≥93.0 %
Rutile content:≥97.0 %
Inorganic coating:Si, Al
TiO₂ content:≥93.0 %
Rutile content:≥97.0 %
Inorganic coating:Zr, Al
Rutile content:≥97.0 %
Loss at 105℃:≤0.50 %
Sieve residue:≤0.01 %
Standard B-type Plastisol Viscosity (mPa·s):2258
Foreign Impurity Particle Count (pcs):4
Volatile Matter (Including Moisture) (%):0.31
TiO₂ Content:94.6
Brightness:95.7
Tinting Strength:1935
TiO₂ Content:96.2%
Rutile Content:98.5%
Density:4.1 g/cm³
TiO₂ Content:94.4%
Brightness:94.8
Drying Loss:0.4%
Loss on drying:0.35%
Water Soluble Matter:0.22%
Sieve Residue:0.012%
Average Polymerization Degree:1342
Foreign Impurity Particles:4 pcs
Volatile Content:0.31%
TiO₂ Content:93.9%
Rutile Content:98.1%
Loss at 105℃:0.30%
Polymerization Degree:1015
Brookfield Viscosity:3720 cps
Foreign Particles:3 pcs/576 cm²
TiO₂ Content:89.0 %
Rutile Content:99.9 %
Dry L* Value:99.3